First, My Specimen Was Scratched, And Now The Mount Has Radial Cracks!

Cracks in your mount are never a welcome sight. While a scratched specimen doesn’t always have a cracked mount, a mount with radial cracks is far more likely to cause a future scratched specimen. While we covered the scratches in an earlier tip, we can’t ignore the cracks.

What causes radial cracks in a metallographic mount?

Most mounting materials do not possess high strength and can be quite brittle. When the cross-sectional area of the mounting material can no longer withstand the stress applied to it, it will fracture. This is most likely to occur where the mounting media layer is thin. It is usually recommended that there be at least a 3 mm (1/8 inch) gap between the specimen and the outside diameter of the mount. Sharp corners on a specimen can also act as stress risers, which contributes to crack initiation. If possible, sharp corners should be rounded off prior to mounting.

Are a few cracks in the mounting material really a problem?

Any crack or gap in a metallographic mount is a place for contaminants to hide. During grinding and/or polishing, liquid, which contains abrasive particles, can be sucked up into cracks and gaps by capillary action. Later, and always at the worst possible moment, these relatively large particles will be drawn out of the crack/gap and onto the polishing cloth. These “bandit” particles will cause objectionable scratches and permanently ruin the effectiveness of the cloth. Liquid drawn up into cracks and gaps can also cause staining of the specimen following etching.

Taking the proper precautions to prevent radial cracks can save you both time and money. If you are still experiencing frequent cracking even after correcting for the above causes, let us know. Contact us at This email address is being protected from spambots. You need JavaScript enabled to view it., and we will have an expert reach out to help you get your lab running smoothly once again.

 

BACK

 

First, My Specimen Was Scratched, And Now The Mount Has Radial Cracks!

LECO Laboratory Equipment and Scientific Instrumentation

Over 85 years of experience in the analytical industry

LECO Corporate Profile Video from LECO Corporation on Vimeo.

We take away the stress and frustration your laboratory experiences when faced with the increasing demands of doing more with less.

The one thing all laboratories need to be successful is results they feel confident in. Since 1936, millions of samples worldwide have been analyzed using LECO instruments for elemental analysis, thermal analysis, metallography, and mass spectrometry. Our comprehensive solutions for improving productivity include working with you to find the right equipment for the type of analysis you are doing — and providing you with the training, application support, and service you need to keep your lab running at its best.

Protein Analysis – Dumas vs. Kjeldahl

May 17, 2022

A Small Overview and Comparison

The protein content in food and feeds is one of the parameters that are commonly analysed within most routine control samples in a food laboratory. Generally, the two most used reference methods/technologies are the wet chemistry method after Kjeldahl and the combustion method after Dumas.

Read More…

Juicing Juice: Determining Protein with the FP928

May 4, 2022

Year after year, the popularity of juice continues to rise. As consumers become more health- and environmentally-conscious, juice has risen to the forefront as a sustainable, vegan, and nutritious beverage option. It certainly doesn't hurt that with the pandemic, people have shifted to entertaining at home and making their own mixed drinks with juices as mixers. But how does juice actually hold up to nutritional demands?

Read More…

MOSH/MOAH Analytics: e-FoodLab Interview with Dr. Susanne Kühn, Kirchhoff Institute

April 26, 2022

Have you seen the article in the latest eFoodLab issue about MOSH/MOAH analytics?
In this interview Dr. Susanne Kühn from our customer
Kirchhoff Institute describes how she uses LECO´s GC×GC-BT-TOF-MS for the characterization of the MOAH fraction. She describes why GC×GC enables a more detailed examination of the MOSH and MOAH fractions.  Interested?

Read More…

Pesky Pesto Peculiarities and GC×GC Analysis

April 13, 2022

Pesto can trace its roots back to ancient times, though it really only started taking off in North America in the 1980s and 90s. Though the primary base is consistent, with pine nuts, basil, and olive oil, individual recipes vary. As canned and bottled pesto became more accessible, individual manufacturers developed their own unique flavor profiles. While these recipes are usually trade secrets, the power of GC×GC TOFMS can tease apart some of the differences.

Read More…